Influence of material type and preparation depth on the fracture resistance of endocrown restoration | ||||
Egyptian Dental Journal | ||||
Article 3, Volume 68, Issue 1 - Serial Number 4, January 2022, Page 597-605 PDF (935.95 K) | ||||
Document Type: Original Article | ||||
DOI: 10.21608/edj.2021.92662.1770 | ||||
View on SCiNiTO | ||||
Authors | ||||
Abdallah Mohamed EL-hosary 1; Walid Al-Zordk 2; abdelreheem abdelkader 3; Mohamed Ghazy 4 | ||||
1fixed prosthodontics, faculty of dentistry Mansoura university | ||||
2Associate Professor, Fixed Prosthodontics Dept., Faculty of Dentistry, Mansoura University, Mansoura, Egypt | ||||
3Assistant Professor, Fixed Prothodontic, Faculty of Dentistry, Mansoura University | ||||
4Professor, Fixed Prosthodontics Department, Mansoura University, Mansoura, Egypt | ||||
Abstract | ||||
Objectives: To assess the impact of intra-coronal preparation depth and restorative material on the fracture resistance of molar restored by endo-crown restoration. Materials and Methods: Forty root canal treated maxillary first molars were prepared for endo-crown restorations. Specimens were divided according to the pulpal extension depth and material type into four groups (n=10): teeth prepared with 3 mm pulpal extension and restored by PEEK (TP); teeth prepared with 3 mm pulpal extension and restored by zirconia (TZ); teeth prepared with 5 mm pulpal extension and restored by PEEK (FP); and teeth prepared with 5 mm pulpal extension and restored by zirconia (FZ). After fabrication of the restorations, each endo-crown was cemented to its corresponding tooth. All specimens were thermo-cycled (5,000 cycles - 5°C and 55°C). Each specimen was loaded till failure using universal testing machine, then the mode of failure was recorded. Two-way ANOVA and Tukey’s post-hoc tests were employed for data analysis (P< .05). Results: The highest fracture load was recorded with FP group (2578.3± 337 N) and the lowest value was recorded with TZ group (1511.42± 168 N). Two-way ANOVA test showed a significant difference among studied groups. Post hoc test showed significant differences between each pair of groups, except a non-significant difference (P = .787) between TZ and FZ groups. Conclusions: The fracture strength of molars restored with endo-crowns can enhanced by increasing the extension depth into pulp chamber. Moreover, PEEK is considered a promising material for endo-crowns. | ||||
Keywords | ||||
Endodontically-treated; Failure; Monolithic; Fracture; Endo-crown | ||||