Evaluation of Marginal Accuracy & Fracture Resistance of Different CAD/CAM Fabricated Monolithic Vonlays | ||||
| Egyptian Dental Journal | ||||
| Volume 70, Issue 1 - Serial Number 4, January 2024, Page 395-402 PDF (1.08 MB) | ||||
| Document Type: Original Article | ||||
| DOI: 10.21608/edj.2023.238829.2724 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
Rasha Sayed Asaad   1; shereen Essameldein Fahim 2; Shereen Kotb Kotb Salem 1
| ||||
| 1Associate Professor, Fixed Prosthodontics, Faculty of Dentistry, October 6 University, Giza, Egypt | ||||
| 2Lecturer, Conservative dentistry, Faculty of Dentistry, October 6 University, Giza, Egypt. | ||||
| Abstract | ||||
| Objective: This research aimed to evaluate & compare marginal accuracy & fracture resistance of three different CAD/CAM fabricated monolithic vonlays. Materials & Methods: A typodont maxillary second premolar was prepared to receive thirty CAD/CAM monolithic vonlays. Three groups of different materials (n=10) were constructed. Group(CD): Zirconia-reinforced lithium silicate (Celtra Duo). Group(VE):Hybrid ceramic(Vita Enamic). Group(BC): Reinforced composite (BRILLIANT Crios). Measurement of vertical marginal gap distance was performed at 16 predetermined points without cementation. Fracture resistance test was conducted for cemented vonlays on their respective epoxy dies. Results: Difference in vertical marginal gap of the three groups was not statistically significant, while fracture resistance showed a significant difference between the three groups. Conclusions: The three tested materials offered vonlays with comparable & clinically acceptable marginal gaps. Concerning the fracture resistance, only Brilliant Crios & Celtra Duo vonlays were proven to have acceptable fracture resistance in premolar area, while Vita Enamic is not recommended as a vonlay in the same area. KEY WORDS: Marginal accuracy, fracture resistance, vonlay, Celtra Duo, Vita Enamic, BRILLIANT Crios. | ||||
| Keywords | ||||
| vonlay; Celtra Duo; Vita Enamic; BRILLIANT Crios | ||||
|
Statistics Article View: 185 PDF Download: 116 |
||||